WEWELDING601H(簡稱威歐丁601H)超級不銹鋼焊條

WEWELDING601H概述:WEWELDING601H(簡稱威歐丁601H)是一種通用的不銹鋼焊條,用于各種級別不銹鋼的高級全方位焊接合金,具有高抗腐蝕性和高耐熱性,耐熱溫度高達1200℃。WEWELDING601H具有良好的焊接性,在各種情況下,極少量的飛濺并易于焊渣清除

WEWELDING601H通用性:
WEWELDING601H可以用來焊修各種級別的不銹鋼及碳鋼,特別是用于焊接310,314,410,430和近似的其它不銹鋼以及其它合金鋼。完全奧氏體結構意味著不會出現西格瑪相。

WEWELDING601H應用舉例:
如:熔爐零件    高溫風機葉片    鋼水包    熱處理容器   高溫管道等等

WEWELDING601H力學性能:
抗拉強度:       達到100,000磅/平方英寸(689牛頓/平方毫米)
屈服強度:       達到 65,000磅/平方英寸(448牛頓/平方毫米)
延伸率           40%
電流類型:       AC/DC+

WEWELDING601H工藝參數:
直徑(㎜)             2.4        3.2           4.0
電流強度(安培)       50-80      70-110        90-150
包裝尺寸(磅)          5         5            5

WEWELDING601H使用提示:
1、保持短弧,維持最大層間溫度為200℃。
2、推薦細長的疊珠焊縫,清除焊層間的焊渣。
3、斜切厚壁截面,形成75度的V型坡口。通常不推薦預熱。

 

WEWELDING601H CHARACTER: 
1.Heat and corrosion resistant alloy for all grades of stainless steel
2.Heat and scale resistant up to 1200℃(2190ºF)
3.Good weldability in all positions with little spatter and easy slag removal.
4.Fully austenitic structure means no risk of sigma phase.
5.Designed for welding 310,314,410,430 and similar stainless steels.

For uses such as:
—furnace parts                      –high temperature fan blades
—ladles                            –heat treating utensils

WEWELDING601H technical data
(Typical Values)
Tensile Strength………………………….up to 100000psi(689kg/mm2)
Yield Strength……………………………up to 65000psi(448 kg/mm2)
Elongation……………………………………………………………40%
Current Type:AC/DC+

WEWELDING601H process parameters
Diameter(mm)       2.4      3.2        4.0
Amperage         50-80     70-110      90-150
Pkg.Size(lb)       5        5         5  

WEWELDING601H Hints
1.Maintain a short arc length and maintain a maximum interpass temperature of 200℃
2.Stringer bead is recommended. Remove slag between passes.
3.Bevel heavy sections to form a 75ºV-groove.Preheat is normally not recommended.
4.CrNi based heat and scale resistant filler materials are not designed to withstand high temperature, sulfur containing fumes. For this reason, the final layer should be welded using a ferritical-chrome steel filler material. Contact R&D Industries for additional information.